Product Description and Application 产品描和用途
This product is a kind of insulation compounds, which can be irradiated and cross-linked. It doesn’t contain heavy metals like Pb, Ba, Cd, Sn and Sb. It can meet ROHS Standard and its cables can pass VW-1 burning requirements. The highest working temperature is 150℃, and is mainly used for various control cables, instrument wires of automotive low-voltage wires, installment wires and electric wires.
该材料是一种可以辐照交联的阻燃绝缘料,不含Pb、Ba、Cd、Cr、Sn、Sb六大重金属, 满足RoHS标准要求，电线能满足VW-1的燃烧要求，最高工作温度150℃。主要用于各类控制电缆，汽车低压电线电缆的仪器仪表, 安装电线电缆，电子线。
 
Processing Indicator 加工工艺
Recommend to use single ordinary screw extruder with L/D=20-25.
建议使用普通单螺杆挤出机进行加工，长径比L/D=20-25。

Model 牌号	Machine Barrel Temperature 机筒温度	Molding Temperature 机头温度
FEJZ105/FEJZ125/FEJZ150	130-140℃	150-160℃

 
 
 
 
Physical and Electrical Properties 物理及电性能指标

Item 试验项目		Unit 单位	Technical requirements 技术要求
			FEJZ105	FEJZ125	FEJZ150
Tensile Strength 拉伸强度		MPa	≥12.5（8.0）	≥12.5（8.0）	≥12.5（8.0）
Elongation at Break 断裂伸长率		%	≥250	≥250	≥250
Density 密度		g/cm3	≤1.35	≤1.35	≤1.35
Dielectric Strength 介电强度		MV/m	≥20	≥20	≥20
Aging Condition 热老化条件		/	136℃×168h	158℃×168h	180℃×168h
Variation of Tensile Strength After Aging 老化后拉伸强度变化率		%	±20	±20	±20
Elongation Variation After Aging 老化后断裂伸长率变化率		%	±20	±20	±20
Brittle Temperature With Low Temperature Impact 低温冲击脆化温度		℃	≤-40	≤-40	≤-40
20℃Volume Resistivity 20℃体积电阻率		/	≥1.0×1012	≥1.0×1012	≥1.0×1012
Hot Set Test Condition热延伸试验条件 200℃×0.2MPa×15min	Hot Elongation 负荷下伸长率	%	≤80	≤80	≤80
	Permanent Deformation after Cooling 冷却后永久形变	%	≤5	≤5	≤5
Oxygen Index 氧指数		%	28	28	28
Burning Level 燃烧等级		/	94-v-0	94-v-0	94-v-0

1、The recommended dose of irradiation pull :12 -18 megabytes. 建议的辐照剂量为：12-18兆拉。
2、The data in（）is measured before irradiation.           （）中的数据为，辐照之前的数据。