90℃热塑性低烟无卤阻燃护套料 TEWR960

90℃ Thermoplastic Low-smoke Halogen-free Flame-retardant Jacketing Compound ...

型号：0

参考价：￥

Description and Application 产品描述和用途
TEWR960 is a kind of thermoplastic low-smoke halogen-free flame-retardant jacketing compounds. It has good mechanical property, high-temperature resistant and processability, especially good irradiation-resistant and aging resistant properties. It is low-smoke and halogen-free, especially suitable for the jacketing which has strict aging property requirements. It is also suitable for the jacketing of K1, K3 nulcear power cables. According to The Arrhenius Equation, this product can reach 90℃and 60-year service life.
TEWR960是热塑性低烟无卤阻燃护套料，其具有优良的物理机械性能，耐高低温性以及加工性能，更为突出的是其具有卓越的耐辐照性和耐热老化性。产品低烟，无卤，特别适用于对老化条件要求较高的电缆绝缘层，适用于制作K1，K3核电用电缆的内绝缘，根据阿累尼乌斯方程推断，本产品符合90℃条件60年寿命的要求。

Processing Indicator 加工工艺
Recommend to use special screw for low-smoke halogen-free compound with L/D=20-25.
采用低烟无卤专用螺杆，长径比L/D=20-25。

Model 牌号	Machine Barrel Temperature 机筒温度	Molding Temprature 机头温度
TEWR960	130-160℃	150-170℃

Physical and Eletrical Properties 物理及电性能指标

试验项目		单位	技术要求
Density 密度		g/cm³	≤1.5
Tensile Strength 抗张强度		MPa	≥10.0
Elongation at Break 断裂伸长率		%	≥250
Aging Conditions 老化条件		/	（110±2）℃×240 h
Changing rate of Tensile Strength 抗张强度变化率		％	≤±20
Changing Rate if Elongation 断裂伸长率变化率		％	≤±20
High Temperature Pressure Test 高温压力试验（80±2℃）		%	≤50
Volume Resistivity of Insulation 绝缘体积电阻率(1kV，20℃)		Ω·m	≥1×10¹²
Brittle Temperature With Low Temperature低温脆化温度		℃	-40
Dielectric Strength 介电强度(1kV，20℃)		kV/mm	≥18
HCL gas Evolution 卤酸气体含量测定		mg/g	≤5
PH Value PH值		/	≥4.3
Conductivity 电导率		μS/mm	≤10
Smoke Density 烟密度	No-flame Mode无焰	%	≤200
	Flame Mode 有焰	%	≤190
Toxicity Index 毒性指数		/	≤2.5
Oxygen Index 氧指数		%	≥30
UV-resistant Test 耐紫外线试验		h	≥720
Material Life（90℃）材料寿命		年	≥60